PRODUCTS

Brands Page

AlphaCast218


General Information
Category Gold
Caratage 14K-18K
Color White
Color Shade Standart White
Typology Alloys For Gold
Production Process İnvestment Casting
Density [cm3] 12,8
Solidus [°C] 900
Liquidus [°C] 955
As cast hardness [HV] 145
Ingredient
  • Ag
  • Cu
  • Zn
  • Ni
  • Deoxidant
  • Grain Refiner
  • Other
Typical Applications
Open System
Closed System
Sheet Production
General Characteristics
As Cast Grain Size [µm] 720
Color Coordinates
L* 84,6
a* 0,9
b* 9,4
c* 9,5
Mechanical Caracteristics
Tensile Strength (Rm) [MPa] 600
Yields strength (Rp0.2) [MPa] 370
Elongation Rupture (A) [%] 33
As cast Hardness [HV] 145
Hardness after 70% area red. [HV] 320
Hardness after annealing [HV] 165
Hardness after age-hardening [HV] 179
Casting Processing Parameters
Pre-mixing temperature [°C] 1100
Casting Temperatures Metal [°C] Flask [°C]
Thin (below 0.5 mm ) 1020 - 1050 660 - 700
Medium ( from 0.5-1.2 mm) 1000 - 1020 620 - 660
Thick (Thick 1.2 mm) 980 - 1000 580 - 620
After casting, cooling time for the flaks is 45 minutes.
After casting, cooling time for the flaks is 15 minutes.
Sulphuric acid (%10) - 5 min - 50°C
Age Hardening Processing Parameters
Single step age-hardening treatment Temperature [°C] Time [min] Quenching Age-hardening
Age-hardening 285 100 Cooling in furnuce