General Information
Category	Gold
Caratage	21K-22K
Color	Yellow
Color Shade	Light Yellow
Typology	Alloys For Gold
Production Process	Universal
Density [cm³]	16,4
Solidus [°C]	935
Liquidus [°C]	990
As cast hardness [HV]	120

Ingredient

Ag Cu Zn Ni Deoxidant Grain Refiner Other

Typical Applications

General Characteristics
As Cast Grain Size [µm]	60

Color Coordinates
L*	85,8
a*	5,4
b*	22
c*	22,65

Mechanical Caracteristics
Tensile Strength (Rm) [MPa]	440
Yields strength (Rp0.2) [MPa]	230
Elongation Rupture (A) [%]	40
As cast Hardness [HV]	120
Hardness after 70% area red. [HV]	215
Hardness after annealing [HV]	125
Hardness after age-hardening [HV]	125

Casting Processing Parameters
Pre-mixing temperature [°C]	1100

Casting Temperatures	Metal [°C]	Flask [°C]
Thin (below 0.5 mm )	1080 - 1110	660 - 720
Medium ( from 0.5-1.2 mm)	1060 - 1080	600 - 660
Thick (Thick 1.2 mm)	1040 - 1060	540 - 600

Trees without stones After casting, cooling time for the flaks is 45 minutes.

Stone-in-place casting trees After casting, cooling time for the flaks is 15 minutes.

Pickling : Sulphuric acid (%10) - 5 min - 50°C

Mechanical Working Parameters

Pre-mixing temperature [°C]	1040-1080
Pickling	Sulphuric Acid (%10)

Casting Temperature	Metal - from [°C]	Metal - to [°C]
Ingot Making	1040	1080
Continuous Casting	1060	1100

Reccomended reductions
Sheet - area or thickness [%]	70
Wire - diameter [%]	45

Mechanical working recommended annealing	Temperature [°C]	Time [min]
> 5 mm	660 - 700	40
1 - 5 mm	660 - 700	30
< 1 mm	660 - 700	20

Age Hardening Processing Parameters
Single step age-hardening treatment	Temperature [°C]	Time [min]	Quenching	Age-hardening
Age-hardening	325	100	Cooling in furnuce